Changing the properties of building mortars with redispersible polymer powders after exposure at high temperatures
Abstract
Changing the properties of building mortars with redispersible polymer powders after exposure at high temperatures
Incoming article date: 06.09.2022The influence of redispersible polymer powders on the change in the properties of building mortars after holding at high temperature in accordance with GOST R 56387-2018 has been studied. An increase in the compressive strength by 10 – 15% was revealed at a dosage of RPP 2 – 3%. It was found that the introduction of an air-entrapping admixture into the composition has a negligible, up to 5%, negative effect on increasing the compressive strength. The increase in the flexural strength after holding at high temperature was 1.5 – 1.8 times. The decrease in the E-modulus practically does not depend on the dosage of RPP. After holding at high temperature, the E-modulus was 0.8 – 0.84 relative to normal hardening conditions. A decrease in the adhesion strength to the concrete base to values of 0.39 – 0.71 relative to normal hardening conditions was revealed. It is noted that the decrease in adhesion strength significantly depends on prescription factors, with the exception of formulations containing an air-entrapping additive, in which there is practically no decrease in adhesion strength after holding at high temperature.
Keywords: redispersible polymer powders, adhesion strength, E-modulus, compressive and flexural strength, high temperature